Observation of room temperature photoluminescence from asymmetric CuGaO2/ Zno/ZnMgo multiple quantum well structures

P. M. Aneesh, M. K. Jayaraj, R. Reshmi, R. S. Ajimsha, L. M. Kukreja, A. Aldrin, F. Rojas, J. Bertomeu, J. López-Vidrier, S. Hernández

Producción: Contribución a una revistaArtículorevisión exhaustiva

2 Citas (Scopus)

Resumen

Asymmetric (CuGaO2 /ZnO/ZnMgO) and symmetric (ZnMgO/ZnO/ZnMgO) multiple quantum well (MQW) structures were successfully fabricated using pulsed laser deposition (PLD) and their comparison were made. Efficient room temperature photoluminescent (PL) emission was observed from these MQWs and temperature dependent luminescence of asymmetric and symmetric MQWs can be explained using the existing theories. A systematic blue shift was observed in both MQWs with decrease in the confinement layer thickness which could be attributed to the quantum confinement effects. The PL emission from asymmetric and symmetric MQW structures were blue shifted compared to 150 nm thick ZnO thin film grown by PLD due to quantum confinement effects.

Idioma originalInglés
Páginas (desde-hasta)3944-3950
Número de páginas7
PublicaciónJournal of Nanoscience and Nanotechnology
Volumen15
N.º5
DOI
EstadoPublicada - 01 may. 2015
Publicado de forma externa

Huella

Profundice en los temas de investigación de 'Observation of room temperature photoluminescence from asymmetric CuGaO2/ Zno/ZnMgo multiple quantum well structures'. En conjunto forman una huella única.

Citar esto